C8830
- Paste Type: Conductor
- Substrate: Glass
- Application Method: Screen Printing
- Application: Hybrid IC
Details
Description
C 8830 is a low temperature, screen printable, pure silver conductor. This pastes exhibits excellent solderability on a wide range of glass substrates with or without coating such as ITO and FTO.
Key Features
Excellent printability
Excellent solder ability and leach resistance
Very good conductivity
Excellent solder ability and leach resistance
Very good conductivity
Metal
Ag
Viscosity
C 8830 25 – 40 Pa·s
(25°C, D = 75 s-1
C 8830A 40 – 55 Pa·s
(25°C, D = 100 s-1)
(25°C, D = 75 s-1
C 8830A 40 – 55 Pa·s
(25°C, D = 100 s-1)
Storage and Paste Preparation
Store in a dry, cool (5 - 25°C), dark place with container tightly shut. Allow paste to come to room temperature prior to opening. Spatulate well before using.
Warranty
Material guaranteed to meet specifications for 3 months from date of manufacturing with proper storage.
Printing Parameters
200 – 400 mesh stainless steel screen
Printing Speed
Up to 20 cm / s
Drying Temperature
Level at room temperature for 5 - 10 minutes.Dry at 150 °C for 10 - 20 minutes
Process Temperature (TDS)
420 – 650 °C (peak) for 10 – 20 minutes, and with a total firing cycle time of c. 30 – 60 minutes
Film Thickness
C 88302 6 -10 µm C 8830A 8 -13 µm (200 mesh screen, 30µm emulsion)