10-074HF
- Paste Type: Component Metallization
- Substrate: PZT, NTC Ceramics, Alumina (Al2O3), Steatite, Porcelain
- Application Method: Screen Printing
- Application: Piezo, Component Metallization
Details
Description
10-074HF is a silver bearing conductor paste designed to screen print solderable electrodes onto a variety of electrical ceramic component devices. The fired film forms a highly adherent bond to many types of substrates, including piezoelectric transducers (PZTs), NTC thermistors, alumina, steatite and porcelain. The metalized electrode is solderable for external lead attachments.
Key Features
Excellent adhesion
Excellent solderability
Compatible on piezoelectric transducers (PZTs), NTC thermistors, alumina, steatite and porcelain
Excellent solderability
Compatible on piezoelectric transducers (PZTs), NTC thermistors, alumina, steatite and porcelain
Metal
Ag
Viscosity
35 – 50 kcps, Brookfield RVT,
Spindle #7, @ 20 rpm, 25°C
Spindle #7, @ 20 rpm, 25°C
Storage and Paste Preparation
Store in a dry location at 15 - 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Printing Parameters
100 – 250 mesh stainless steel screen
0.3 – 1.0 mil emulsion
0.3 – 1.0 mil emulsion
Drying Temperature
100 - 150 ºC for 10 - 15 minutes
Process Temperature (TDS)
725 – 850ºC peak temperature
Dwell time of 8 – 12 minutes at peak temperature
Cycle time of 45 – 60 minutes
Larger parts may require a longer firing profile
Dwell time of 8 – 12 minutes at peak temperature
Cycle time of 45 – 60 minutes
Larger parts may require a longer firing profile
Film Thickness
5 – 9 µm