6082
6082
Open modal
Paste Type:
Component Metallization
Substrate:
Alumina (Al2O3), Zirconia (ZnO2), Titania (TiO2)
Application Method:
Brushing, Spraying
Application:
Sensors
Get in contact
Download Datasheet
PDF
Details
Open all
Close all
Description & Key Features
Description
6082 is a reactive (metal oxide) bonded platinum paste, which fires to a dense fired surface. 6082 has a rheology suitable for brushing.
Key Features
Chemical resistant Fritless, reactive bond paste Brushable viscosity Can be used on Alumina, Zirconia or Titania bodies
Paste Properties
Metal
Pt
Viscosity
4620 – 6200 cps Brookfield RVTSC4 – 14 spindle, 6R utility cup at 50 rpm, 25 °C
Coverage
190 cm2/gram
Coverage
190 cm2/gram
Storage and Paste Preparation
Store in a dry location at 5 – 25 °C
Warranty
3 months
Processing
Printing Parameters
280 mesh stainless steel screen. 0.5 mil emulsion_x000D_
Drying Temperature
125°C peak temperature 15 minutes at peak temperature
Process Temperature (TDS)
850 – 1100°C peak temperatureDwell time of 9 – 11 minutes
Film Thickness
Wet: 20 - 25 microns Dried: 10 - 14 microns Fired: 5 – 9 microns