867B is a low temperature firing silver conductor paste. 867B is formulated for use on glass and alumina.
Key Features
Low firing temperature Excellent solderability Low resistivity
Metal
Ag
Viscosity
60 - 80 Kcps Brookfield HBT, SC4-14 spindle and 6R utility cup @ 10 rpm, 25oC
Coverage
99 cm2/gram at 12 microns fired film thickness
Coverage
99 cm2/gram at 12 microns fired film thickness
Storage and Paste Preparation
Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Process Temperature (TDS)
510 - 540°C peak temperature Dwell time of 3 - 4 minutes