C2103M
- Paste Type: Conductor
- Substrate: Alumina (Al2O3)
- Application Method: Screen Printing
- Application: Fuel Level Senders
Details
Description
C2103M is a Pd/Ag Conductor paste which exhibits high density, high reliability and good fine line definition, (6 mil lines and spaces). It fires to a smooth surface and is mechanically durable and chemically resistant. Conductivity, leach resistance, and resistance to silver migration are exceptional. Due to these characteristics pastes such as C2103M are frequently preferred material for fuel level sensor applications.
Key Features
Excellent solderability and leach resistance
Exceptional silver migration resistance
Smooth fired surface
Exceptional silver migration resistance
Smooth fired surface
Metal
AgPd
Viscosity
180 – 240 kcps, Brookfield HBT, SC4-14 spindle & 6R utility cup @ 10 rpm, 25°C
Coverage
84 cm²/g at 12 μm fired film thickness
Coverage
84 cm²/g at 12 μm fired film thickness
Storage and Paste Preparation
Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Printing Parameters
280 – 325 mesh stainless steel screen
0.5 mil emulsion, 1.1 mil wire
Let the print level at room temperature for 10 minutes before
drying
0.5 mil emulsion, 1.1 mil wire
Let the print level at room temperature for 10 minutes before
drying
Printing Speed
up to 6 in/sec
Drying Temperature
150 °C for 10 minutes
Process Temperature (TDS)
850 °C peak for 10 minutes,Total cycle time 30 – 60 minutes
Film Thickness
Wet: 34 – 38 µmDried: 18 – 22 µmFired: 10 – 13 µm