C4350
- Paste Type: Conductor
- Substrate: Alumina (Al2O3)
- Application Method: Screen Printing
- Application: Hybrid IC, Sensors
Details
Description
C4350 is an Au conductor incorporating a low melting frit. This gold is suitable for low firing applications such as glass displays and soda lime substrate structures. C4350 is supplied in a screen printing viscosity.
Key Features
Low firing temperature High conductivity Screen printable
Metal
Au
Viscosity
230 – 270 kcps Brookfield HBT, Spindle #14 @ 10 rpm, 25°C
Coverage
55 cm2/g at 12 µm fired film thickness
Coverage
55 cm2/g at 12 µm fired film thickness
Storage and Paste Preparation
Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Printing Parameters
325 mesh stainless steel screen 0.5 mil emulsion
Drying Temperature
150 °C for 5 - 10 minutes
Process Temperature (TDS)
525 – 650 °C peak temperature Dwell time of 5 – 6 minutes at peak
Film Thickness
10 – 14 μm