PCC11913

Description

PCC11913 is a Pb and Cd free low temperature firing silver paste designed to screen print solderable electrodes onto a variety of electrical ceramic component devices. The fired film forms a highly adherent bond to many types of substrates, including piezoelectric transducers (PZTs), NTC thermistors, alumina, steatite, and porcelain. The metalized electrode is readily solderable for external lead attachment.

Key Features

Lower firing temperature (< 700 ºC)

Metal

Ag

Viscosity

80 – 100 Kcps, Brookfield HBT SC4-14 and 6R utility cup at 10 rpm, 25 °C

Storage and Paste Preparation

Store in a dry location at 5 – 25 °C

Warranty

6 months

Printing Parameters

80 – 200 stainless steel mesh screens 0.7 – 1.0 mil emulsion Allow parts to level at room temperature before drying

Drying Temperature

150 ºC for 10 – 15 minutes

Process Temperature (TDS)

Optimum firing parameters depend on substrate composition 650 – 700 ºC peak firing temperature Dwell time of 8 – 12 minutes Total cycle time of 45 – 60 minutes Larger parts may require a longer firing profile_x000D_

Film Thickness

9 – 15 µm