PCC11972

Description

PCC11972 is a low temperature firing silver paste
designed to screen print solderable electrodes onto a
variety of electrical ceramic component devices. The fired
film forms a highly adherent bond to many types of
substrates, including piezo-electric transducers (PZTs),
NTC thermistors, alumina, steatite, and porcelain. The
metalized electrode is solderable for external lead
attachment.

Key Features

RoHS compliant*
REACH compliant**
Lower firing temperature (< 700°C)
Designed for piezo-electric transducers (PZTs),
NTC thermistors, alumina, steatite, and porcelain
substrates

Metal

Ag

Viscosity

24 - 30 Kcps Brookfield RVT, Spindle #7 @ 20 rpm,
25°C _x000D_

Storage and Paste Preparation

Store in a dry location at 5 – 25 °C

Warranty

6 months

Printing Parameters

60-200 mesh stainless steel screen
0.7-1.0 mil emulsion.
Allow parts to level at room temperature for 5 – 10 minutes
before drying.

Drying Temperature

150°C for 10 minutes

Process Temperature (TDS)

650°C -700°C peak firing temperature
Dwell time of 8-12 minutes at peak
Total cycle time of 45-60 minutes.

Film Thickness

9 - 15 microns