The PCR12000 series is a lead-free resistor series that was developed for applications which require peak firing temperatures lower than traditional thick film resistors series. The PCR12000 series is formulated to fire at a 590°C peak firing temperature, which makes this series suitable for substrates such as glass for plasma display panels (PDP). The PCR12000 Series is also compatible with the Heraeus Celcion material set.
Key Features
Low temperature 590 °C firing Formulated to fire on glass
Metal
Viscosity
PCR12035 and PCR12038 150 – 200 kcps, Brookfield HBT, SC4-14 spindle & 6R utility cup @ 10 rpm , 25°C PCR12045, PCR12019 and PCR12020 180 – 220 kcps, Brookfield HBT, SC4-14 spindle & 6R utility cup @ 10 rpm, 25°C
Coverage
Coverage
Storage and Paste Preparation
Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Printing Parameters
165 – 325 mesh, 1.1 mil wire and 0.5 mil emulsion screen Allow prints to level for 5 – 10 minutes at room temperature
Printing Speed
Up to 10 in/sec (25 cm/sec)
Drying Temperature
Dry at 150 ºC for 8 - 10 minutes
Process Temperature (TDS)
Firing range between 550 – 650 ºC Recommended 590 ºC peak temperature with a 10 minutes dwell time Total cycle time of 30 minutes