6082

Description

6082 is a reactive (metal oxide) bonded platinum paste, which fires to a dense fired surface. 6082 has a rheology suitable for brushing.

Key Features

Chemical resistant
Fritless, reactive bond paste
Brushable viscosity
Can be used on Alumina, Zirconia or Titania bodies

Metal

Pt

Viscosity

4620 – 6200 cps Brookfield RVT, SC4-14 spindle & 6R utility cup @ 50 rpm, 25°C

Coverage

190 cm2/gram

Coverage

190 cm2/gram

Storage and Paste Preparation

Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.

Warranty

Material guaranteed to meet specifications for 3 months from date of manufacturing with proper storage.

Printing Parameters

280 mesh stainless steel screen.
0.5 mil emulsion

Drying Temperature

125°C peak temperature, 15 minutes at peak temperature

Process Temperature (TDS)

850 – 1100°C peak temperatureDwell time of 9 – 11 minutes

Film Thickness

Wet: 20 - 25 microns Dried: 10 - 14 microns Fired: 5 – 9 microns