C2160

Description

C2160 is a Pd/Ag composition designed for hybrid applications and application where more leach resistance is required. The C2160 conductor is suitable for a wide variety of applications such as automotive electronics, power hybrids and commercial application where more stringent requirement exist. It exhibits excellent solderability, aged adhesion properties and is aluminum wire bondable.

Key Features

Excellent solderability and leach resistance
Excellent long term adhesion
Good AI wire bond adhesion (initial and aged)

Metal

AgPd

Viscosity

150 – 220 kcps, Brookfield HBT, SC4-14 spindle & 6R utility cup, @ 10 rpm, 25°C

Coverage

80 cm²/g at 12 μm fired film thickness

Coverage

80 cm²/g at 12 μm fired film thickness

Storage and Paste Preparation

Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.

Warranty

Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.

Printing Parameters

280 – 325 mesh stainless steel screen
0.5 mil emulsion
Allow to level at room temperature for 5 – 10 minutes before
drying

Printing Speed

Up to 7 in/sec

Drying Temperature

150 °C for 10 to 15 minutes

Process Temperature (TDS)

850 °C peak temperature10 minutes at peakTotal cycle time 30 – 60 minutes

Film Thickness

10 – 15 μm