C4310
- Paste Type: Conductor
- Substrate: Alumina (Al2O3)
- Application Method: Screen Printing
- Application: Hybrid IC
Details
Description
C4310 is a 6/1 Ag/Pd fritted conductor which exhibits excellent solder acceptance, leach resistance and aged adhesion. C4310 has been specifically formulated for use on dielectric.
Key Features
Wide processing parameters
High adhesion on dielectric
Excellent refire stability
High adhesion on dielectric
Excellent refire stability
Metal
AgPd
Viscosity
190-250 kcps Brookfield HBT,
#14 spindle@ 10 rpm, 25°C. _x000D_
#14 spindle@ 10 rpm, 25°C. _x000D_
Coverage
70 cm2
/g at 14 microns fired film thickness
/g at 14 microns fired film thickness
Coverage
70 cm2
/g at 14 microns fired film thickness
/g at 14 microns fired film thickness
Storage and Paste Preparation
Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Printing Parameters
325 stainless steel mesh screen
0.5 mil emulsion
1.1 mil wire
0.5 mil emulsion
1.1 mil wire
Drying Temperature
150°C for10 minutes.
Process Temperature (TDS)
850°C peak temperature
Dwell time of 9-11 minutes
Dwell time of 9-11 minutes
Film Thickness
12-16 microns