C5799
- Paste Type: Conductor
- Substrate: Alumina (Al2O3)
- Application Method: Screen Printing
- Application: Hybrid IC
Details
Description
C5799 is a screen printable gold via fill conductor designed for use in multilayer hybrids. It is designed to be used with either IP9117 or IP9118. It gives excellent surface coplanarity along with good electrical conductivity.
Key Features
Outstanding via fill to dielectric adhesion Excellent surface coplanarity Good conductivity Easy to process Ideal interface for Au bearing conductors
Metal
Au
Viscosity
250 – 400 kcps, Brookfield HBT, SC4-14 spindle & 6R utility cup @ 10 rpm, 25°C
Coverage
68 cm2
/g at 25 µm fired film thickness
/g at 25 µm fired film thickness
Coverage
68 cm2
/g at 25 µm fired film thickness
/g at 25 µm fired film thickness
Storage and Paste Preparation
Store in a dry, cool (5 - 25°C), dark place with container tightly shut. Allow paste to come to room temperature prior to opening. Spatulate well before using.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Printing Parameters
325 mesh stainless steel screen
0.8 mil emulsion
0.8 mil emulsion
Drying Temperature
150 ºC for 10 minutes
Process Temperature (TDS)
875 °C peak temperatureDwell time of 8 – 12 minutes
Film Thickness
20 – 26 μm