IP9105HT

Description

IP9105HT is an insulating glaze used for porcelain steel coating applications and high temperature applications. IP9105HT was specifically designed for use in circuits exposed to operating temperatures in the 475 °C range. IP9105HT may be used in conjunction with Heraeus high temperature resistor systems and conductor materials.

Key Features

High temperature dielectric§Can be used on a wide variety of substrates including steel Standard resistors and conductors are compatible on top

Metal

None

Viscosity

270 – 330 kcps, Brookfield HBT, SC4-14 spindle & 6R utility cup @ 10 rpm, 25°C

Coverage

190 cm2/g at 11 μm wet film thickness

Coverage

190 cm2/g at 11 μm wet film thickness

Storage and Paste Preparation

Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.

Warranty

Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.

Printing Parameters

325 mesh stainless steel screen
0.5 mil emulsion
1.1 mil wire
Two layers each fired individually is recommended for
optimum yield.

Printing Speed

 

Drying Temperature

150 ºC for 10 minutes

Process Temperature (TDS)

915 °C peak temperature Dwell time of 8 – 10 minutes

Film Thickness

Dried: 20 µm
Fired: 11 µm