PC10391
- Paste Type: Conductor
- Substrate: PZT, NTC Ceramics, Alumina (Al2O3), Steatite, Porcelain
- Application Method: Screen Printing
- Application: Sensors, Component Metallization
Details
Description
PC10391 is a high glass content gold conductor. PC10391 is used in sensor applications and provides a dense fired film.
Key Features
Optimized for sensor applications
Excellent printing properties
High glass content paste
Excellent printing properties
High glass content paste
Metal
Au
Viscosity
190 – 240 kcps, Brookfield HBT, SC4-14 spindle & 6R utility cup @ 10 rpm, 25°C
Storage and Paste Preparation
Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.
Warranty
Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.
Printing Parameters
325 stainless steel mesh screen
0.5 mil emulsion
Allow parts to level for 10 – 15 minutes before drying, but
parts should be dried as soon as possible after leveling to
prevent skinning, which can compromise adhesion. Wet
parts should be covered if not dried right away.
0.5 mil emulsion
Allow parts to level for 10 – 15 minutes before drying, but
parts should be dried as soon as possible after leveling to
prevent skinning, which can compromise adhesion. Wet
parts should be covered if not dried right away.
Drying Temperature
150°C for 10 minutes Make sure ventilation is sufficient to prevent the wet film from skinning.
Process Temperature (TDS)
850°C peak temperature
Dwell time of 10 minutes at peak
Total cycle time of 45 - 60 minutes
Dwell time of 10 minutes at peak
Total cycle time of 45 - 60 minutes
Film Thickness
8-14 microns