ST1609

Description

ST1609 is a silver metallization developed for lead zirconate titanate (PZT) ceramic bodies. It will fire to a dense film for maximum capacitance. ST1609 also has excellent adhesion and solderability. ST1609 is supplied at a viscosity for screen printing. The organic system will give a screen life of greater than 4 hours.

Key Features

Customer formulated for use on PZT ceramics
Screen printable
Excellent solderability and adhesion
REACH1 compliant

Metal

Ag

Viscosity

195 – 345 kcps Brookfield LVT
#5 spindle, @ 3 rpm, 25°C_x000D_

Storage and Paste Preparation

Store in a dry location at 5 – 25°C. DO NOT REFRIGERATE. Allow paste to come to room temperature prior to opening. Spatulate well before using, as settling may occur during storage.

Warranty

Material guaranteed to meet specifications for 6 months from date of manufacturing with proper storage.

Printing Parameters

165 – 200 mesh stainless steel screen
0.5 mil emulsion

Drying Temperature

150 °C for 10 minutes

Process Temperature (TDS)

550 – 650 °C peak temperature
Dwell time of 5 – 7 minutes at peak